Table 2.1 · Thesis 4 · Orayech 2015

Table 2.1 · Thesis 4 · Orayech 2015

status thesis-only · visibility public · id tbl:thesis-04.2.1

Last temperature treatment (\mathrm{K}) and duration (\mathrm{h}) for the \mathrm{A}_{2} \mathrm{MSbO}_{6} compounds.

Document
Thesis 4 · Orayech 2015
Table
2.1
Compound Temperature (K) Duration (h)
\mathrm{Sr}_{2} \mathrm{NdSbO}_{6} 1570 72
\mathrm{Sr}_{2} \mathrm{EuSbO}_{6} 1570 72
\mathrm{Sr}_{2} \mathrm{GdSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{DySbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{HoSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{YSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{ErSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{TmSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{YbSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{InSbO}_{6} 1770 72
\mathrm{Sr}_{2} \mathrm{In}_{0.25} \mathrm{Sc}_{0.75} \mathrm{SbO}_{6} 1770 48
\mathrm{Sr}_{2} \mathrm{In}_{0.5} \mathrm{Sc}_{0.5} \mathrm{SbO}_{6} 1770 48
\mathrm{Sr}_{2} \mathrm{In}_{0.75} \mathrm{Sc}_{0.25} \mathrm{SbO}_{6} 1770 48
\mathrm{Ca}_{2} \mathrm{NdSbO}_{6} 1770 72
\mathrm{Ca}_{2} \mathrm{EuSbO}_{6} 1770 72
\mathrm{Ca}_{2} \mathrm{GdSbO}_{6} 1820 72
\mathrm{Ca}_{2} \mathrm{DySbO}_{6} 1770 72
\mathrm{Ca}_{2} \mathrm{HoSbO}_{6} 1820 72
\mathrm{Ca}_{2} \mathrm{YSbO}_{6} 1820 48
\mathrm{Ca}_{2} \mathrm{ErSbO}_{6} 1870 72
\mathrm{Ca}_{2} \mathrm{TmSbO}_{6} 1870 48
\mathrm{Ca}_{2} \mathrm{YbSbO}_{6} 1820 72
\mathrm{Ca}_{2} \mathrm{InSbO}_{6} 1820 48