Crystal chemistry of \mathrm{SrLnMRuO}_{6}(\mathrm{Ln}=\mathrm{La}, \mathrm{Pr}, \mathrm{Nd}; \mathrm{M}=\mathrm{Zn}, \mathrm{Co}, \mathrm{Cu}, \mathrm{Mg}, \mathrm{Ni}) perovskites [115, 116, 120] at room temperature.
| t^{a} | t_{0}{ }^{b} | A_{0}{ }_{8}{ }^{c} | <A-\mathrm{O}>{ }_{\text {8short }}{ }^{d} | <A-\mathrm{O}>_{4 \text { long }}{ }^{e} | A \mathrm{O}_{12}{ }^{f} | \Psi_{[001] M}{ }^{g} | \Psi_{[001] \mathrm{Ru}}{ }^{h} | \Phi_{[110] M}{ }^{i} | \Phi_{[110] \mathrm{Ru}}{ }^{j} | \mathrm{GM}_{4}^{+k} | \mathrm{X}_{3}^{+l} | \mathrm{X}_{5}^{+m} | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Crystal chemistry of \operatorname{SrPr} M \mathrm{PuO}_{6}(\mathrm{M}=\mathrm{Zn}, \mathrm{Co}, \mathrm{Ni}, \mathrm{Mg}) | |||||||||||||
| Zn | 0.8933 | 0.913(1) | 27.71(1) | 2.60(1) | 3.22(1) | 51.95(1) | 7.5(2) | 9.6(2) | 11.3(3) | 12.0(3) | 1.155(4) | 0.843(5) | 0.404(4) |
| Co | 0.8955 | 0.920(1) | 27.54(1) | 2.60(1) | 3.18(1) | 51.32(1) | 7.1(2) | 8.6(2) | 11.3(2) | 11.7(2) | 1.094(4) | 0.777(5) | 0.378(7) |
| Ni | 0.9043 | 0.823(1) | 27.44(1) | 2.60(1) | 3.15(1) | 51.92(1) | 7.2(2) | 8.3(1) | 10.4(2) | 10.8(2) | 1.075(4) | 0.761(5) | 0.338(6) |
| Mg | 0.8977 | 0.928(1) | 27.79(1) | 2.62(1) | 3.14(1) | 51.32(1) | 9.2(1) | 5.9(1) | 10.4(3) | 10.4(3) | 1.026(4) | 0.737(6) | 0.285(6) |
| Crystal chemistry of \mathrm{SrNd} \mathrm{MRuO}_{6}(\mathrm{M}=\mathrm{Zn}, \mathrm{Co}, \mathrm{Ni}, \mathrm{Mg}) [120] | |||||||||||||
| Zn | 0.8801 | 0.911(1) | 27.56(1) | 2.60(1) | 3.23(1) | 51.77(1) | 10.40(8) | 7.00(9) | 11.8(2) | 12.6(2) | 1.200(3) | 0.855(4) | 0.425(3) |
| Co | 0.8823 | 0.919(1) | 27.37(1) | 2.60(1) | 3.18(1) | 51.04(1) | 6.6(1) | 9.6(1) | 11.0(2) | 11.8(2) | 1.122(4) | 0.790(5) | 0.365(5) |
| Ni | 0.8909 | 0.923(1) | 27.33(1) | 2.60(1) | 3.15(1) | 51.62(1) | 9.4(1) | 5.6(1) | 12.0(3) | 12.9(3) | 1.152(5) | 0.733(6) | 0.376(6) |
| Mg | 0.8844 | 0.922(1) | 27.43(1) | 2.61(1) | 3.15(1) | 51.02(1) | 5.7(1) | 9.4(1) | 11.4(2) | 11.8(2) | 1.109(4) | 0.737(5) | 0.335(6) |
| Crystal chemistry of \mathrm{SrLa} M R u O_{6}(\mathrm{M}=\mathrm{Co}, \mathrm{Cu}, \mathrm{Ni}) [115][116] | |||||||||||||
| Co | 0.9018 | 0.933(1) | 28.20(1) | 2.64(1) | 3.12(1) | 51.69(1) | 7.7(1) | 4.8(1) | 10.5(2) | 10.9(2) | 1.01(1) | 0.62(1) | 0.274(7) |
| Cu | 0.9014 | 0.93(1) | 28.10(1) | 2.64(1) | 3.12(1) | 51.67(1) | 7.0(4) | 5.8(5) | 10.9(6) | 11.5(7) | 1.04(6) | 0.63(5) | 0.26(4) |
| Ni | 0.9103 | 0.93(1) | 28.98(1) | 2.64(1) | 3.10(1) | 51.18(1) | 4.8(2) | 7.6(2) | 10.0(4) | 10.4(5) | 1.00(4) | 0.60(3) | 0.27(2) |