perovskite atlas Structures, modes and phase transitions · Josu M. Igartua · UPV/EHU

Figure 9.2 · Thesis 3 · Iturbe 2012

Figure 9.2 · Thesis 3 · Iturbe 2012

status thesis-only · visibility public · id plt:thesis-03.9.2

Experimental (symbols) and calculated (line) neutron powder-diffraction profiles for the Rietveld refinement of \mathrm{SrLnFeRuO}_{6}(\mathrm{Ln}=\mathrm{La}, \mathrm{Nd}, \mathrm{Pr}) at room temperature, using a disordered orthorhombic (Pbnm) structural model. The upper (middle) markers indicate the position of the structural (magnetic) Bragg reflections and the lower markers the impurity ( \mathrm{Nd}_{3} \mathrm{RuO}_{7} and \mathrm{Pr}_{3} \mathrm{RuO}_{7}) Bragg reflections. \mathrm{La}_{3} \mathrm{RuO}_{7} impurity was excluded in order to guarantee the convergence of the refinement.

Experimental (symbols) and calculated (line) neutron powder-diffraction profiles for the Rietveld refinement of \mathrm{SrLnFeRuO}_{6}(\mathrm{Ln}=\mathrm{La}, \mathrm{Nd}, \mathrm{Pr}) at room temperature, using a disordered orthorhombic (Pbnm) structural model. The upper (middle) markers indicate the position of the structural (magnetic) Bragg reflections and the lower markers the impurity ( \mathrm{Nd}_{3} \mathrm{RuO}_{7} and \mathrm{Pr}_{3} \mathrm{RuO}_{7}) Bragg reflections. \mathrm{La}_{3} \mathrm{RuO}_{7} impurity was excluded in order to guarantee the convergence of the refinement.

Document
Thesis 3 · Iturbe 2012
Figure
9.2
Kind
rietveld-plot
Rights
own
Reproduce
not-needed

auto-cropped from the OCR Markdown crop box (stage B); materials and kind to be reviewed in Phase 1

Evidence