Experimental (symbols) and calculated (line) neutron powder-diffraction profiles (D2B \lambda=1.594 \AA) for the Rietveld refinement of \mathrm{SrPr} \mathrm{MRuO}_{6}(\mathrm{M}=\mathrm{Zn}, \mathrm{Co}, \mathrm{Mg}, \mathrm{Ni}) at room temperature, using a structural model with the space group P 2_{1} / n. The bars in the lower part of the graphics correspond to the Bragg-reflections’ positions. In the case \mathrm{SrPrNiRuO}_{6}, the lower set of bars correspond to the impurity \mathrm{NiO}(3.75(6) \%).

Experimental (symbols) and calculated (line) neutron powder-diffraction profiles (D2B \lambda=1.594 \AA) for the Rietveld refinement of \mathrm{SrPr} \mathrm{MRuO}_{6}(\mathrm{M}=\mathrm{Zn}, \mathrm{Co}, \mathrm{Mg}, \mathrm{Ni}) at room temperature, using a structural model with the space group P 2_{1} / n. The bars in the lower part of the graphics correspond to the Bragg-reflections’ positions. In the case \mathrm{SrPrNiRuO}_{6}, the lower set of bars correspond to the impurity \mathrm{NiO}(3.75(6) \%).

Document
Thesis 3 · Iturbe 2012
Figure
6.2
Kind
rietveld-plot
Rights
own
Reproduce
not-needed

auto-cropped from the OCR Markdown crop box (stage B); materials and kind to be reviewed in Phase 1

Evidence